Details Sample Characterization



Mineral: Corundum
Reference: QMC15
Preparation: Nano alumina was synthesized using following procedure: alumina precursor (aluminum tri-sec-butoxide dissolved in dichloromethane, ACROS organic) was added into the self-assembly templates (pluronic surfactant-P123, BASF corporation NJ) under vigorous stirring conditions. The nano alumina was obtained by heating it at 550 °C for 12 h.
Crystallinity: wormhole-like
Sample characterized via: ☑ Transmission electron microscopy (TEM)
☑ X-ray Diffraction (XRD)
Comment: nano alumina
 