Details Sample Characterization
Mineral: |
Palygorskite |
Reference: |
PHCLW18 |
Preparation: |
ATP (50 g) was activated with 500 mL H2O2 and 250 mL HCl (1 M) for 2 h to remove metal cations and residual carbon in the crystal backbone of ATP. After exhaustive washing with deionized water and ethanol, the activated ATP was dried for 24 h at 80°C under vacuum. Fe(III)/ATP nanoparticles were synthesized by the ultrasonic co-precipita-
tion method (Liu et al. 2008). The activated ATP (0.7 g) was dispersed into 200 mL of 0.2 M FeCl3 solution or 200 mL mixture solution for 3 h with continuous ultrasound stirring. 1 M NaOH was then added dropwise to the mixture until pH~11.0. The precipitations were filtered, washed with deionized water to pH 7.0, dried at 70°C for 24 h, and then fired at 450°C in muffle furnace. |
Composition: |
iron-content: 25.6 % |
Sample characterized via: |
☑ X-ray photoelectron spectroscopy (XPS)
☑ FT-IR spectroscopy
☑ Energy-dispersive X-ray spectroscopy (EDX)
☑ Scanning electron microscope (SEM)
☑ X-ray Diffraction (XRD)
|
Comment: |
Fe(III)/ATP, uniform reddish brown colour |
|
1 data sets were retrieved
|