1 PublikationSc3AlN - A New Perovskite
Höglund, C.; Birch, J.; Beckers, M.; Alling, B.; Czigány, Z.; Mücklich, A.; Hultman, L.
Abstract
Sc3AlN with perovskite structure has been synthesized as the first ternary phase in the Sc-Al-N system. Magnetron sputter epitaxy at 650 °C was used to grow single-crystal, stoichiometric Sc3AlN(111) thin films onto MgO(111) substrates with ScN(111) seed layers as shown by elastic recoil detection analysis, X-ray diffraction, and transmission electron microscopy. The Sc3AlN phase has a lattice parameter of 4.40 Å, which is in good agreement with the theoretically predicted 4.42 Å. Comparisons of total formation energies show that Sc3AlN is thermodynamically stable with respect to all known binary compounds. Sc3AlN(111) films of 1.75 µm thickness exhibit a nanoindentation hardness of 14.2 GPa, an elastic modulus of 249 GPa, and a room-temperature electrical resistivity of 41.2 µΩ cm.
-
European Journal of Inorganic Chemistry 8(2008), 1193-1195
DOI: 10.1002/ejic.200701356
Cited 25 times in Scopus
Permalink: https://www.hzdr.de/publications/Publ-10997
Jahre: 2023 2022 2021 2020 2019 2018 2017 2016 2015